Welcome to The Wight Brick Company. A very small manufacturer of handmade and mini bricks from Isle of Wight and Yorkshire clay on the Isle of Wight |
|
|
|
The History of Bricks and Brickmaking. Bricks are one of the oldest known building materials dating back to 7000BC where they were first found in southern Turkey and around Jericho. The first bricks were sun dried mud bricks. Fired bricks were found to be more resistant to harsher weather conditions, which made them a much more reliable brick for use in permanent buildings, where mud bricks would not have been sufficient. Fired brick were also useful for absorbing any heat generated throughout the day, then releasing it at night The Ancient Egyptians also used sun dried mud bricks as building materials, evidence of which can still be seen today at ruins such as Harappa Buhen and Mohenjo-daro. Paintings on the tomb walls of Thebes portray slaves mixing, tempering and carrying clay for the sun dried bricks. These bricks also consisted of a 4:2:1 ratio which enabled them to be laid more easily. The Romans further distinguished those which had been dried by the sun and air and those bricks which were burnt in a kiln. Preferring to make their bricks in the spring, the Romans held on to their bricks for 2 years before they were used or sold. They only used clay which was whitish or red for their bricks. The Greeks also considered perpendicular brick walls more durable than stone walls and used them for public edifices. They also realised how the modern brick was less susceptible to erosion than the old marble walls. During the 12th century bricks were reintroduced to northern Germany from northern Italy. This created the brick gothic period which was a reduced style of Gothic architecture previously very common in northern Europe. The buildings around this time were mainly built from fired red clay bricks. Brick Gothic style buildings can be found in the Baltic countries Sweden, Denmark, Poland, Germany, Finland, Lithuania, Latvia, Estonia, Belarus and Russia. The brick gothic period can be categorized by the lack of figural architectural sculptures which had previously been carved in stone. The Gothic figures were impossible to create out of bulky bricks at that time, but could be identified by the use of split courses of bricks in varying colours, red bricks, glazed bricks and white lime plaster. Eventually special shaped bricks were introduced which would imitate the architectural sculptures. Bricks now Bricks are more commonly used in the construction of buildings than any other material except wood. Brick and terracotta architecture is dominant within its field and a great industry has developed and invested in the manufacture of many different types of bricks of all shapes and colours. With modern machinery, earth moving equipment, powerful electric motors and modern tunnel kilns, making bricks has become much more productive and efficient. Bricks can be made from variety of materials the most common being clay but also calcium silicate and concrete. With clay bricks being the more popular, they are now manufactured using three processes soft mud, dry press and extruded. Also during 2007 the new ‘fly ash’ brick was created using the by-products from coal power plants. Good quality bricks have a major advantage over stone as they are reliable, weather resistant and can tolerate acids, pollution and fire. Bricks can be made to any specification in colour, size and shape which makes bricks easier to build with than stone. Brickwork is also much cheaper than cut stone work. However there are some bricks which are more porous and therefore more susceptible to dampness when exposed to water. For best results in any construction work, the correct brick must be chosen in accordance with the job specifications. Building bricks are a mixture of clay and sand which is mixed with water to create the correct consistency. Sometimes the bricks also have added lime, ash or organic matter which speeds up the burning of the brick. The clay mixture is then formed in moulds to the desired specification ready to be dried then burnt in the kiln. Clay: The properties and quality of bricks depend on the type of clay used. The most common form of clay used for everyday bricks, is that with a sandy consistency, silicate or alumina, which usually contains small quantities of lime or iron oxide. Silica, when added to pure clay in the form of sand, prevents cracking, shrinking and warping. If there is a large proportion of sand used in the mixture the brick will be more textured and shapely. An excess of sand, however, renders the bricks too brittle and destroys cohesion. 25% of silica is said to be advantageous. Iron oxide in the clay enables the silica and alumina to fuse and adds considerably to the hardness and strength of the bricks. The iron content of the brick is evident in the colour of the brick and can be used to add the colour red into the bricks. However a clay which burns to a red colour will provide a stronger brick than clay which burns to a white or yellow brick. The lime content in a brick has two different effects. It stops the raw brick from shrinking and drying out, and it also acts as a flux during burning which causes the silica to melt and creates the bond which binds all the components of the brick together. However, too much lime can cause the brick to melt and loose shape. Any amount of quicklime within a brick is detrimental to its quality and can cause the brick to split into pieces. For the best qualities of pressed brick the clay is carefully selected both colour and composition. Clay from different sources is also often mixed together to create the desired mixture. Handmade bricks used to be very commonly used throughout the UK. The process involves putting the clay, water and additives into a large pit where it is all mixed together by a tempering wheel generally still powered by horse power. Once the mixture is of the correct consistency, the clay is removed and pressed into moulds by hand. To prevent the brick from sticking to the mould, the brick is coated in either sand or water. Named ‘slop moulding’ when dipped in water and ‘sand struck’ when coated in sand. Coating the brick with sand however gives an overall better finish to the brick. Once shaped, the bricks are laid outside to dry by air and sun where they will be drying for three to four days. After this process the bricks are then transferred to the kiln for burning. If green bricks are left outside for the drying process and are left out during a shower; the water leaves an indentation of the brick is considered very undesirable. However this does not affect the strength properties of the bricks. Bricks are now more generally made by large scale manufacturing processes using machinery. This is a large scale effort and produces bricks which have been burned in patent kilns. There are three different types of manufacturing process for machine made bricks - the soft mud process, the stiff mud process and the dry clay process for which machines are specifically designed. The ‘Soft mud ‘process is similar to that of handmade bricks. In the Soft Mud process that clay contains too much water to be extruded as the clay is left to soak in water for 24 hours. For this process three pits are usually in operation at any one time to keep the production flowing. Occasionally the clay is worked in a pug mill before being thrown into the machine. Due to the 20% water content of the clay, wooden moulds are generally used and are lined with either oil or sand to stop the clay sticking. After being drawn from the machine the filled moulds are emptied by hand and the bricks taken to the dry shed. So the soft mud bricks can be dried properly, both handmade soft mud bricks and machine made (more mass produced) bricks will both be placed in a large dryer which is separate from the extrusion dryer. The ‘Stiff mud’ process differs because only enough water to create plasticity is added to the clay, approximately 12% water. Clay is then extruded through a ‘die’ to produce a long stream of pressed clay which is then cut to size by the machine. The die sizes and cutter wire are calculated to compensate for the shrinkage of the brick during drying and firing. Attachments can also be added to the die which gives the brick its texture from brush, roll, and scratch to roughen. Green bricks are then dried out carefully to ensure a consistent colour and strength. Because Soft Mud bricks have been created under little or no pressure, their density is not as great as that of Stiff Mud bricks. It has been argued that when Soft Mud bricks have been made and burned properly they are possibly the most durable brick. However Stiff mud bricks can have defects or planes of separation which can affect the bricks durability. However as Stiff Mud bricks are becoming increasingly cheaper to produce these are becoming the more popular. The ‘Repressing’ of a brick is to re-shape the brick or round of any corners dependent on specification. Both types of soft mud and stiff mud bricks can be repressed when they are only partially dried. This is done by placing the bricks in metal moulds and putting them under great pressure before burning. Pressed bricks however are machine moulded bricks where the clay being used is already nearly dry. This process can make a significant difference on the appearance of the bricks. Bricks made using this process generally are more difficult to compress. Dry pressed bricks however are now commonly used for face bricks. Pressed bricks generally mean dry pressed bricks, but many face bricks are made by repressing soft mud bricks. ‘Cement’ bricks made from Portland cement, these bricks are machine moulded into size and shape to match the size of clay bricks. These are extensively used in some regions. ‘Hollow, Terracotta or Tile’. This type of product can made into practically and size or shape for any kind of use. Blocks made of terra-cotta are light and durable. For use in partitions the terra-cotta is mixed with sawdust which burns off in the kiln, but creates a more porous brick. Terra-cotta can be glazed or unglazed. Facing bricks are uniform in colour and shape and can now be made to any almost any specification, texture, colour and size. Wirecut extruded bricks. For this type of brick the clay is extruded and cut by wore into individual bricks. This is a very cost effective way of producing bricks and is done by an automated production process. These bricks are readily available in a variety of styles and colours. Stock bricks; are usually slightly more expensive than wirecut Bricks. These are a soft mud brick which are sometimes irregular in shape. Handmade bricks; as previously discussed above, handmade bricks are very desirable and individual in shape and colour. This brick is one of the most expensive sorts of brick. Fletton or London Brick; is a brick made from clay extracted from the south east of England which contains traces of oil which is burnt off during the burning process in the kiln. Arch and Clinker bricks This term is used for bricks which are burned immediately. They are over burnt and sometimes distorted in shape. Body, Cherry and/or hard bricks. These bricks are of a higher quality and are generally the bricks that were in the centre of the pile of bricks which have been burned. These bricks are top bricks as they have a higher overall quality and finish. Cherry is used as a term when the clay which has been used burns red. Salmon, Pale or Soft bricks. These are the bricks which were nearer to the outside of the kiln during burning which means they are slightly under burnt. These bricks are generally softer than the bricks taken from the centre of the kiln are therefore are of a lesser quality, although this does not affect the overall shape of the brick. These bricks are generally used for the interior of walls. Waterstruck Brick This type of brick is a soft mud moulded brick. It uses alluvial clay which deposited at the end of the last ice age. The clay is pressed into mould lined with silicate. When the bricks are removed from their mould, they are left with a textured effect which can only be achieved using this method. This type of brick looks old and handmade even when new. Engineering Bricks Engineering bricks are called so due to their overall strength and water absorption. The Class A brick has strength of 125N/mm² and water absorption of less than 4.5%. Class B engineering bricks have a strength greater than 75N/mm² and water absorption of less than 7%. Traditionally used in civil engineering, these bricks are also useful for damp courses and structural design. Bullnose Bricks These special bricks are used when round edges are needed, for gate recesses, quadrants or arches. Off Shades or Seconds or ATR or Random Quality. These are batches of bricks which are generally consistent in colour but do not match the product which is marketed. Different uses for bricks Dependant on their final use, the bricks are named accordingly. Brick Sizes Metric and Imperial 215 × 102.5 × 50 Standard Metric215 × 102.5 × 65 Metric 225 × 107.5 × 67 Imperial 230 × 110 × 70 Imperial 230 × 110 × 73 Imperial 230 × 110 × 76 Imperial 230 × 110 × 80 Although in the UK, the depth used to be less (about 2 ins/51mm) whereas modern bricks are about 2.5 ins/64mm.
Brick cuttingis the process of cutting bricks into the desired size or in most cases to cut and bond them together using an epoxy mortar to form angle bricks these are mainly used on bay windows and conservatories etc. Thermal Efficiency and Compliance with Building Regulations http://www.bbacerts.co.uk/ Kiln Brick Burning
The Scotch Kiln is the most commonly used in the UK. This is a rectangular building which is open at the top and has side doors with fireholes built from fire bricks. The kilns will contain approximately 80, 000 bricks at full capacity. Raw bricks are arranged in the kiln leaving gaps in between each brick to ensure an even burn. It takes approximately three days to burn off the moisture from the bricks, at which point the firing is increased for the final burn. It takes between 48 and 60 hours to completely burn a brick to achieve its maximum strength. As mentioned before the bricks from the centre of kiln will be of the highest quality whilst the ones from the edges are sometimes clinkered and unsuitable for exterior work.
Lime Mortar Slaked lime is used to make lime mortar. The mortar is made by mixing sand with slaked lime at the proportion of 1 part lime to 5 parts sand. There are two types of lime used in lime mortars, one that sets and hardens by the reaction with the air (non-hydraulic) and one which sets by reaction to the water (hydraulic). Hydraulic Limes. Calcium carbonates naturally occur but can include some impurities. It is these impurities which when burned in a kiln create the calcium silicates or aluminates that react with water to set. Enough water is added to the mixture to create calcium hydroxide powder form. The hydraulic lime is then graded depending on their overall set strength. White and Coloured Mortar White and coloured mortars should be made using lime putty and screened sand. Colour is created by adding additional minerals to the white mortar. Coloured mortars are not as strong as white mortars. However the more popular mortar colours are red, brown, buff and black, green, purple and grey. Brick Tinting from Bricks UK available at http://www.extensionmatch.co.uk/motartinting.html Brick tinting has been used for decades by brick and masonry manufacturers and also by many developers on new house sites when there are problems between different batches of manufactured bricks, delivered on site which causes slight shade and colour differences between one lorry load of bricks and another. Tinting is then used to match the affected bricks to the colour of the original bricks, seamlessly blending the different batches together. Brick tinters do not "paint" the brick with pre-set coloured paints, the process is a chemical and oxide solution involving various colour dyes. Each match is unique and the dye is mixed on site by our specialists once they have assessed the required colours to match, including and varying blends.Matching and creating the colour on site ensures that we get the exact colour dye solution to match your individual brick in your individual situation. Brickwork Bonds Stretcher bond This bond is the most commonly used today. Bricks used to make this bond are just half a English Bond An English bond has alternating courses of headers and stretchers. The alternative headers Flemish Bond This bond has alternating headers and stretchers along each course. The headers should be
This bond is very similar to the English Bond but its headers run one in every six courses of
This type of bond is used for walls which need to be curved. It is made by full bricks laid Pointing Different types of Pointing Weather Struck Joint Weather Struck and Cut Pointing Similar to the previous weather struck joint, except the bed joints are neatly trimmed using a Frenchman or pointing trowel. Tooled, Bucket Handel Joint The most popular joint used today, where the joint bed is slightly rounded inwards. The mortar should not be pressed in too hard. The tool needed for this job is a rubber hose, an old type bucket handle. Flush or Rag Joint This finish of this joint is flush with the brick work, smoothed off with a rag. This finish should only be used for brickwork above water level. Recessed Joints This Finish of this joint is recessed. The mortar is formed to a consistence depth of approximately 5 mm. This joint should only be used with a frost resistant brick and is not recommended where the brickwork could be exposed to severe wind driven rain.
With thanks to www.expressbrick.com
|
||||||
A new book marks the diversity of England's chimneypots. Gaze up at their beauty. |
© The Wight Brick Company 2012 - 2016 |
|||||
Search Engine Optimization and SEO Tools |
|||||